Alumold500 aerospace aluminum alloy is an important application in mold manufacturing

Alumold500 aluminum alloy is an aluminum alloy material specially used for the production of injection molds. Alumold 500 aluminum alloy provides greater strength, stability and durability compared to other 7000 series aluminum mold plates and forged materials.

Chemical composition of Alumold500:

Cu: 0.15-0.4

Si: 0.4-0.8,

Fe: 0.7-,0.13< /p>

Mn0.15-0.50,

Mg: 0.8-1.2

Zn: 0.25-0.50

Cr: 0.04-0.35

p>

Ti: 0.15

Density is 2.72g/cm3

Mechanical properties:

Tensile strength (25°CMPa)

Yield strength (25°CMPa)

Hardness 500kg force 10mm ball

Elongation 1.6mm (1/16in) thickness

Note: Pipe room temperature Longitudinal mechanical properties

Different properties in different states.

Alumold500 aluminum alloy has high strength and can withstand high pressure and impact during the injection mold manufacturing process. It maintains a stable shape and provides a long service life, reducing deformation and damage caused by stress. In addition, Alumold500 aluminum alloy also has good stability and can provide stable mold temperature and shape control during the injection molding process. It can quickly conduct and disperse heat, evenly distribute the temperature of the mold, and avoid problems caused by local overheating or undercooling.

The durability of Alumold500 aluminum alloy also makes it an ideal choice for injection mold manufacturing. It resists the high pressure, abrasion and chemical corrosion associated with the injection molding process, extending the life of the mold and reducing the need for repairs and replacements.

In general, Alumold500 aluminum alloy, as a material specially used for injection mold manufacturing, has high strength, stability and durability. It meets the important requirements for mold material properties in the injection molding process and provides reliable and long-lasting mold manufacturing solutions.