In-depth exploration of the application of AlMn1Mg0.5 aviation aluminum alloy in the manufacturing of high-strength wear-resistant parts

Summary of the characteristics and applications of AlMn1Mg0.5 aluminum alloy:

Chemical composition

Aluminum Al: balance

Silicon Si: ≤0.40

p>

Copper Cu: ≤0.10

Magnesium Mg: 4.0～4.9

Zinc Zn: ≤0.25

Manganese Mn: 0.40～1.0

p>

Titanium Ti: ≤0.15

Chromium Cr: 0.05～0.25

Iron Fe: 0.000～0.400

Note: Single: ≤0.05;

Total: ≤0.15

Mechanical properties of AlMn1Mg0.5 aluminum plate

Mechanical properties:

Tensile strength σb (MPa) 173~ 244

Conditional yield strength σ0.2 (MPa)≥70

Features: Aviation superhard aluminum alloy: AlMn1Mg0.5 aluminum alloy is called aviation superhard aluminum alloy, indicating that it Has excellent abrasion resistance and anti-wear properties. This means that the alloy is capable of high durability and service life when exposed to wear and friction.

High-strength and wear-resistant parts manufacturing: Due to the characteristics of AlMn1Mg0.5 aluminum alloy, it is suitable for manufacturing high-strength and wear-resistant parts in the aviation field. This includes the manufacture of engine parts, aircraft structural components and wear-resistant components required in aviation equipment. The alloy's high strength and wear-resistant properties allow it to withstand high stress and wear while maintaining structural stability.

Application: Aviation field: AlMn1Mg0.5 aluminum alloy is mainly used in the aviation field. It can be used to manufacture aircraft engine parts (such as blades, blisks, etc.), aircraft structural components (such as fuselage, wing spars, etc.) and wear-resistant parts of other aviation equipment. The alloy's super hardness and wear-resistant properties enable it to meet the high strength and durability requirements of the aviation industry.